Zhao G., Bian W., Nishii J.
Ключевые слова: HTS, YBCO, thin films, TFA-MOD process, substrate LaAlO3, gamma irradiation, fabrication, heat treatment, oxygen, critical caracteristics, Jc/B curves, irradiation effects, experimental results
IEEE Transactions Applied Superconductivity, 2020, v.30, N 1, p.6000205
Полный текст на Sci-Hub
Дополнительная информация
Chen Y., Li L., Zhao G., Tang X., Wu H., Bian W., Li N., Nishii J.
Ключевые слова: coated conductors, fabrication, substrate Ni-W, buffer layers, precursors, X-ray diffraction, microstructure, HTS, YBCO, fluorine process, solution techniques, critical caracteristics, Jc/B curves
J Sol-Gel Science Technology, 2017, v.82, N 2, p.586-593
Zhao G., Lei L., Wu C., Nishii J., Duan Z.
Ключевые слова: HTS, YBCO, multilayered structures, fabrication, sol gel process, thin films, substrate LaAlO3, X-ray diffraction, microstructure, magnetization, resistive transition, resistivity, temperature dependence, critical caracteristics, current-voltage characteristics
J Superconductivity Novel Magnetism, 2017, v.30, N 7, p.1719-1725
Chen Y., Li L., Zhao G., Yan F., Huang W., Fujioka M., Bian W., Li N., Nishii J., Kaiju H.
Ключевые слова: HTS, YBCO, solution techniques, precursors, TFA route, substrate LaAlO3, thin films, films thick, fabrication, microstructure, critical current density, composition, grain alignment, X-ray diffraction, phase composition
Ceramics International, 2017, v.43, N 11, p.8433-8439